G.657.A2 Ukugoba I-Optical Fiber Yemodi Eyodwa Engazweli
Izimo Zohlelo Lokusebenza
Izici Zokusebenza
Ukucaciswa Komkhiqizo
Ipharamitha | izimo | Amayunithi | inani |
I-Optical | |||
Ukunciphisa | 1310 nm | dB/km | ≤ 0.350 |
1383 nm | dB/km | ≤ 0.350 | |
1550 nm | dB/km | ≤ 0.210 | |
1625 nm | dB/km | ≤ 0.230 | |
I-Attenuation vs. Wavelength | 1310 nm VS. 1285- 1330 nm | dB/km | ≤ 0.05 |
1550 nm VS. 1525- 1575 nm | dB/km | ≤ 0.04 | |
I-Zero Dispersion Wavelength | - | nm | 1300-1324 |
I-Zero Dispersion Slope | ps/(nm2 ·km) | 0.073-0.092 | |
Ukuhlakazeka | 1550nm | ps/(nm ·km) | 13.3- 18.6 |
1625nm | ps/(nm ·km) | 17.2-23.7 | |
Ukuhlakazeka kwemodi ye-Polarization (PMD) | - | ps/√km | ≤ 0.2 |
I-Wavelength enqunyiwe λcc | - | nm | ≤ 1260 |
I-Mode Field Diameter (MFD) | 1310 nm | μm | 8.6±0.4 |
1550 nm | μm | 9.6±0.5 | |
Ukunqamuka Ukuyeka | 1310 nm | dB | ≤ 0.03 |
1550 nm | dB | ≤ 0.03 | |
Ijometri | |||
I-Cladding Diameter | μm | 125±0.7 | |
I-Cladding Non-Circularity | % | ≤ 0.8 | |
Iphutha le-Core/Cladding Concentricity | μm | ≤ 0.5 | |
Ububanzi Bokumboza (Okunganemibala) | μm | 242±7 (okujwayelekile) | |
μm | 200±10 (uma uthanda) | ||
Iphutha Le-Coating/Cladding Concentricity | μm | ≤ 12 | |
I-Curl | m | ≥ 4 | |
Ezemvelo (1550nm, 1625nm) | |||
I-Temperature Cycling | -60 ℃ ukuze +85 ℃ | dB/km | ≤ 0.05 |
High Temperature & High Umswakama | 85℃, 85% RH, izinsuku ezingama-30 | dB/km | ≤ 0.05 |
Ukucwiliswa emanzini | 23 ℃, izinsuku ezingu-30 | dB/km | ≤ 0.05 |
Izinga Lokushisa Eliphezulu Ukuguga | 85℃, izinsuku ezingama-30 | dB/km | ≤ 0.05 |
Omakhenikha | |||
Ubufakazi Ukucindezeleka | - | I-GPa | 0.69 |
I-Coating Strip Force * | Isiqongo | N | 1.3 - 8.9 |
Isilinganiso | N | 1.0-5.0 | |
Amandla Okuqina | I-Fk=50% | I-GPa | ≥ 4.00 |
Fk= 15% | I-GPa | ≥ 3.20 | |
Ukukhathala Okunamandla (Nd) | - | - | ≥ 20 |
Ukulahlekelwa Kwe-Macrobending | |||
Ø30 mm×10 t | 1550 nm | dB | ≤ 0.03 |
1625 nm | dB | ≤ 0.1 | |
Ø20 mm×1 ihora | 1550 nm | dB | ≤ 0.1 |
1625 nm | dB | ≤ 0.2 | |
Ø15 mm×1 t | 1550 nm | dB | ≤ 0.4 |
1625 nm | dB | ≤ 0.8 | |
* Amandla epeak amakhasi e-coating ngu-0.6-8.9N, futhi inani elijwayelekile lingu-0.6-5.0N lapho ububanzi bokumboza bungu-200±10. |