G.657.A2 Bending merhatikeun Single-mode serat optik

Parameter

kaayaan

Hijian

nilai

Optik

Atenuasi

1310 nm

dB/km

≤ 0,350

1383 nm

dB/km

≤ 0,350

1550 nm

dB/km

≤ 0,210

1625 nm

dB/km

≤ 0,230

Atenuasi vs Panjang gelombang

1310 nm VS. 1285-1330 nm

dB/km

≤ 0,05

1550 nm VS. 1525-1575 nm

dB/km

≤ 0,04

Nol Dispersi Panjang Gelombang

-

nm

1300-1324

Enol dispersi lamping

ps/(nm2 · km)

0.073-0.092

Panyebaran

1550nm

ps/(nm · km)

13.3- 18.6

1625nm

ps/(nm · km)

17.2-23.7

Polarisasi Mode Dispersi

(PMD)

-

ps/√ km

≤ 0.2

Cut-off Panjang Gelombang λcc

-

nm

≤ 1260

Diaméter Widang Mode (MFD)

1310 nm

μm

8.6±0.4

1550 nm

μm

9.6±0.5

Atenuasi Discontinuity

1310 nm

dB

≤ 0,03

1550 nm

dB

≤ 0,03

Géometri

Diaméterna cladding

μm

125±0,7

Cladding Non-Circularity

%

≤ 0,8

Kasalahan Inti / Cladding Concentricity

μm

≤ 0,5

Diaméter palapis (teu warna)

μm

242±7 (standar)

μm

200±10 (opsional)

Palapis / Cladding Kasalahan Concentricity

μm

≤ 12

Ngagulung

m

≥ 4

Lingkungan (1550nm, 1625nm)

Ngabuburit Suhu

-60 ℃ nepi ka + 85 ℃

dB/km

≤ 0,05

Suhu Luhur & Luhur

Kalembaban

85 ℃, 85% RH, 30 poé

dB/km

≤ 0,05

Cai Immersion

23 ℃, 30 poé

dB/km

≤ 0,05

Sepuh Suhu Tinggi

85 ℃, 30 poé

dB/km

≤ 0,05

Mékanis

Buktina Stress

-

GPa

0.69

Gaya Jalur Palapis *

Puncak

N

1.3 - 8.9

Rata-rata

N

1.0-5.0

Kakuatan regangan

Fk=50%

GPa

≥ 4.00

Fk = 15%

GPa

≥ 3.20

Kacapean Dinamis (Nd)

-

-

≥ 20

Leungitna Macrobend

Ø30 mm × 10 t

1550 nm

dB

≤ 0,03

1625 nm

dB

≤ 0.1

Ø20 mm × 1 h

1550 nm

dB

≤ 0.1

1625 nm

dB

≤ 0.2

Ø15 mm × 1 t

1550 nm

dB

≤ 0.4

1625 nm

dB

≤ 0,8

* Puncak gaya mesek palapis nyaeta 0.6-8.9N, sarta nilai rata-rata 0.6-5.0N lamun diaméter palapis nyaeta 200±10.