G.657.A2 Fibre Optical Fibre Optical mode tokana tsy miforitra
Fampiharana Scenarios
Performance Features
Product Specification
fikirana | NATREHINAY | vondrona | SAROBIDY |
Optical | |||
Attenuation | 1310 nm | dB/km | ≤ 0,350 |
1383 nm | dB/km | ≤ 0,350 | |
1550 nm | dB/km | ≤ 0,210 | |
1625 nm | dB/km | ≤ 0,230 | |
Atenuation vs. halavan'ny onjam | 1310 nm VS. 1285-1330 nm | dB/km | ≤ 0.05 |
1550 nm VS. 1525-1575 nm | dB/km | ≤ 0.04 | |
Ny halavan'ny onjam-pielezana aotra | - | nm | 1300-1324 |
Aotra fiparitahana slope | ps/(nm2 ·km) | 0.073-0.092 | |
pielezana | 1550nm | ps/(nm ·km) | 13.3- 18.6 |
1625nm | ps/(nm ·km) | 17.2-23.7 | |
Fomba fanaparitahana polarization (PMD) | - | ps/√ km | ≤ 0.2 |
Fahatapahan'ny onjam-peo λcc | - | nm | ≤ 1260 |
Savaivony saha mode (MFD) | 1310 nm | μm | 8.6±0.4 |
1550 nm | μm | 9.6±0.5 | |
Attenuation Discontinuity | 1310 nm | dB | ≤ 0.03 |
1550 nm | dB | ≤ 0.03 | |
Geometric | |||
Cladding Diameter | μm | 125±0.7 | |
Cladding Non-Circularity | % | ≤ 0.8 | |
Error Concentricity Core/Cladding | μm | ≤ 0.5 | |
Savaivony coating (tsy miloko) | μm | 242±7 (manara-penitra) | |
μm | 200±10 (tsy voatery) | ||
Fahadisoan'ny Coating/Cladding Concentricity | μm | ≤ 12 | |
Curl | m | ≥ 4 | |
Tontolo iainana (1550nm, 1625nm) | |||
Temperature Cycling | -60 ℃ hatramin'ny + 85 ℃ | dB/km | ≤ 0.05 |
Temperature avo & avo Hamandoana | 85 ℃, 85% RH, 30 andro | dB/km | ≤ 0.05 |
Fandrobohana rano | 23 ℃, 30 andro | dB/km | ≤ 0.05 |
Fahanterana amin'ny hafanana avo | 85 ℃, 30 andro | dB/km | ≤ 0.05 |
Mekanika | |||
Porofo adin-tsaina | - | GPa | 0.69 |
Coating Strip Force * | TAMPON'ISAN'NY | N | 1.3 - 8.9 |
Average | N | 1.0-5.0 | |
Faharetana amin'ny sintona | Fk=50% | GPa | ≥ 4.00 |
Fk= 15% | GPa | ≥ 3.20 | |
Havizanana Dinamika (Nd) | - | - | ≥ 20 |
Fatiantoka Macrobend | |||
Ø30 mm × 10 t | 1550 nm | dB | ≤ 0.03 |
1625 nm | dB | ≤ 0.1 | |
Ø20 mm × 1 ora | 1550 nm | dB | ≤ 0.1 |
1625 nm | dB | ≤ 0.2 | |
Ø15 mm × 1 t | 1550 nm | dB | ≤ 0.4 |
1625 nm | dB | ≤ 0.8 | |
* Ny tampon'isa Peel hery ny coating dia 0.6-8.9N, ary ny eo ho eo ny sanda dia 0.6-5.0N rehefa coating savaivony dia 200±10. |