Spesifikasyon nan fib optik (G.652D)
KALITE
Fib kouch yo ta dwe gratis nan fant, fann, bul, pik elatriye likidasyon yo ta dwe inifòm sou bobin la.
MATERYÈL
Dope silica / silica ak doub kouch UV geri résine.
Spesifikasyon pwodwi
| Sr. Oke. | Paramèt | UoM | Valè |
| 1 | Atténuation | ||
| 1.1 | Nan 1310 nm | dB/km | ≤0.340 |
| 1.2 | Nan 1550 nm | ≤0.190 | |
| 1.3 | Nan 1625 nm | ≤0.210 | |
| 1.4 | Nan 1383±3 nm | ≤valè nan 1310nm | |
| 1.5 | Devyasyon atténuation nan ranje 1525 ~ 1575nm (Ref. 1550nm longèdonn) | dB | ≤0.05 |
| 1.6 | Devyasyon atténuation nan ranje 1285 ~ 1330nm (Ref. 1310nm longèdonn) | ≤0.05 | |
| 2 | Dispèsyon kromatik | ||
| 2.1 | 1285 ~ 1330 nm ranje longèdonn | ps/nm.km | ≤3.5 |
| 2.3 | Nan 1550 nm | ≤18 | |
| 2.4 | Nan 1625 nm | ≤22 | |
| 2.5 | Zewo dispèsyon longèdonn | Nm | 1300 pou 1324 |
| 2.6 | Pant dispèsyon nan longèdonn dispèsyon zewo | nm^2.km | ≤0.092 |
| 3 | PMD | ||
| 3.1 | PMD nan 1310 nm & 1550 nm (fib endividyèl) | ps/sqrt.km | ≤0.10 |
| 3.2 | Link PMD | ≤0.06 | |
| 4 | Koupe longèdonn | ||
| A | Fibre koupe ranje longèdonn | Nm | 1100 ~ 1320 |
| B | Kab koupe longèdonn | ≤1260 | |
| 5 | Dyamèt jaden mòd | ||
| 5.1 | Nan 1310 nm | µm | 9.2±0.4 |
| 5.2 | Nan 1550 nm | 10.4±0.5 | |
| 6 | Pwopriyete jewometrik | ||
| 6.1 | Dyamèt kouch (fib ki pa gen koulè) | µm | 242±5 |
| 6.2 | Dyamèt CLADDING | 125±0.7 | |
| 6.3 | Erè Konsantrisite Nwayo | ≤0.5 | |
| 6.4 | Cladding Non-sikilarite | % | ≤0.7 |
| 6.5 | Coating-Cladding konsantrisite | µm | ≤12 |
| 6.6 | Fib Curl (reyon koub) | Mtr. | ≥4 |
| 6.7 | Pwofil Endèks refraktif | Etap | |
| 6.8 | Endèks gwoup efikas nan refraksyon Neff@1310nm (tip.) | 1.4670 | |
| 6.9 | Endèks gwoup efikas nan refraksyon Neff@1550nm (tip.) | 1.4681 | |
| 7 | Pwopriyete mekanik | ||
| 7.1 | Tès prèv pou min. nivo souch & Dire tès la | kpsi.sec | ≥100 |
| 7.2 | Chanjman nan atenuasyon ak koube (Micro-bend) | ||
| a | 1 vire sou 32mm Dia. Mandrin nan 1310 & 1550 nm | dB | ≤0.05 |
| b | 100 vire sou 60mm Dia. Mandrin nan 1310 & 1550 nm | ≤0.05 | |
| 7.3 | Strippability Fòs yo retire kouch prensipal la | N | 1.0≤F≤8.9 |
| 7.4 | Fòs Tensile dinamik (0.5 ~ 10 mtr. Fib ki pa gen laj) | kpsi | ≥550 |
| 7.5 | Fòs Tensile dinamik (0.5 ~ 10 mtr. Fib ki gen laj) | ≥440 | |
| 7.6 | Fatig dinamik | ≥20 | |
| 8 | Pwopriyete anviwònman an | ||
| 8.1 | Atenuasyon pwovoke nan 1310 & 1550 nm Temp. & Sik imidite soti nan -10 ℃ a + 85 ℃ nan 98% RH (Ref. Tanperati 23 ℃) | dB/km | ≤0.05 |
| 8.2 | Atenuasyon pwovoke nan 1310 & 1550 nm Temp. sik soti -60 ℃ a + 85 ℃ (Ref. Tanperati 23 ℃) | ≤0.05 | |
| 8.3 | Atenuasyon pwovoke nan 1310 & 1550 nm pou Immersion dlo nan 23±2 ℃ | ≤0.05 | |
| 8.4 | Atenuasyon pwovoke nan 1310 & 1550 nm pou aje akselere nan 85±2 ℃ (Ref. Tanperati 23 ℃) | ≤0.05 | |