Spesifikaasje fan Optical Fiber (G.652D)
KWALITEIT
Fiber coating moat wêze frij fan skuorren, spjalten, bubbels, spits ensfh winding moat wêze unifoarm op 'e spool.
MATERIAAL
Gedoteerde silika / silika mei dûbele lagen UV-hurde hars.
Produkt Spesifikaasje
Sr. Goed. | Parameters | UoM | Wearden |
1 | Attenuation | ||
1.1 | Op 1310 nm | dB/km | ≤0,340 |
1.2 | Op 1550 nm | ≤0.190 | |
1.3 | Op 1625 nm | ≤0.210 | |
1.4 | Op 1383±3 nm | ≤wearde op 1310nm | |
1.5 | Attenuation ôfwiking binnen 1525 ~ 1575nm berik (Ref. 1550nm golflingte) | dB | ≤0,05 |
1.6 | Attenuation ôfwiking binnen 1285 ~ 1330nm berik (Ref. 1310nm golflingte) | ≤0,05 | |
2 | Chromatyske dispersion | ||
2.1 | 1285 ~ 1330 nm golflingte berik | ps/nm.km | ≤3.5 |
2.3 | Op 1550 nm | ≤18 | |
2.4 | Op 1625 nm | ≤22 | |
2.5 | Zero dispersion golflingte | Nm | 1300 oant 1324 |
2.6 | Dispersion Slope op nul dispersion golflingte | nm^2.km | ≤0,092 |
3 | PMD | ||
3.1 | PMD by 1310 nm & 1550 nm (yndividuele glêstried) | ps/sqrt.km | ≤0.10 |
3.2 | Link PMD | ≤0,06 | |
4 | Snij de golflingte ôf | ||
IN | Fiber ôfsnien golflingte berik | Nm | 1100~1320 |
B | Kabel ôfsnien golflingte | ≤1260 | |
5 | Mode Field Diameter | ||
5.1 | Op 1310 nm | µm | 9,2±0,4 |
5.2 | Op 1550 nm | 10,4±0,5 | |
6 | Geometryske eigenskippen | ||
6.1 | Coating Diameter (un-coloured fiber) | µm | 242±5 |
6.2 | Bekleding Diameter | 125±0,7 | |
6.3 | Core Concentricity Flater | ≤0.5 | |
6.4 | Cladding Non-circularity | % | ≤0,7 |
6.5 | Coating-Cladding Concentricity | µm | ≤12 |
6.6 | Fiber Curl (krommeradius) | Mtr. | ≥4 |
6.7 | Refractive Index profyl | Stap | |
6.8 | Effektive groepyndeks fan refraksje Neff@1310nm (typ.) | 1.4670 | |
6.9 | Effektive groepyndeks fan refraksje Neff@1550nm (typ.) | 1.4681 | |
7 | Meganyske eigenskippen | ||
7.1 | Bewiistest foar min. strain nivo & Duration fan test | kpsi.sec | ≥100 |
7.2 | Feroaring yn attenuation mei bûgen (Micro-bend) | ||
in | 1 kear op 32mm Dia. Mandrel op 1310 & 1550 nm | dB | ≤0,05 |
b | 100 oansette 60mm Dia. Mandrel op 1310 & 1550 nm | ≤0,05 | |
7.3 | Strippability Force te fuortsmite primêre coating | N | 1.0≤F≤8.9 |
7.4 | Dynamic Tensile Strength (0,5 ~ 10 mtr. Unaged fiber) | kpsi | ≥550 |
7.5 | Dynamic Tensile Strength (0.5~10 mtr. Aged fiber) | ≥440 | |
7.6 | Dynamic Fatigue | ≥20 | |
8 | Miljeu Eigenskippen | ||
8.1 | Induced attenuation by 1310 & 1550 nm Temp. & Feuchte syklus fan -10 ℃ oant +85 ℃ by 98% RH (Ref. temperatuer 23 ℃) | dB/km | ≤0,05 |
8.2 | Induced attenuation by 1310 & 1550 nm Temp. syklus fan -60 ℃ oant +85 ℃ (Ref. temperatuer 23 ℃) | ≤0,05 | |
8.3 | Induced attenuation by 1310 & 1550 nm foar Water Immersion by 23±2 ℃ | ≤0,05 | |
8.4 | Induced attenuation by 1310 & 1550 nm foar Accelerated Aging by 85±2 ℃ (Ref. temp 23 ℃) | ≤0,05 |