G.657.A1. Ukugoba I-Optical Fiber Engazweli Imodi Eyodwa
Izimo zohlelo lokusebenza
Izici Zokusebenza
Ukucaciswa Komkhiqizo
| Ipharamitha | izimo | Amayunithi | inani |
| I-Optical | |||
| Ukunciphisa | 1310 nm | dB/km | ≤ 0.350 |
| 1383 nm | dB/km | ≤ 0.350 | |
| 1550 nm | dB/km | ≤ 0.210 | |
| 1625 nm | dB/km | ≤ 0.230 | |
| I-Attenuation vs. Wavelength | 1310 nm VS. 1285- 1330 nm | dB/km | ≤ 0.04 |
| 1550 nm VS. 1525- 1575 nm | dB/km | ≤ 0.03 | |
| I-Zero Dispersion Wavelength | - | nm | 1300 - 1324 |
| I-Zero Dispersion Slope | ps/(nm2 ·km) | 0.073 - 0.092 | |
| Ukuhlakazeka | 1550nm | ps/(nm ·km) | 13.3- 18.6 |
| 1625nm | ps/(nm ·km) | 17.2-23.7 | |
| I-Polarization Mode Dispersion (PMD) | - | ps/√km | ≤ 0.2 |
| I-Wavelength enqunyiwe λcc | - | nm | ≤ 1260 |
| I-Mode Field Diameter (MFD) | 1310 nm | μm | 9.2±0.4 |
| 1550 nm | μm | 10.4±0.5 | |
| Ukunqamuka Ukuyeka | 1310 nm | dB | ≤ 0.03 |
| 1550 nm | dB | ≤ 0.03 | |
| Ijometri | |||
I-Cladding Diameter |
μm |
125±0.7 |
|
I-Cladding Non-Circularity |
% |
≤ 1.0 |
|
Iphutha le-Core/Cladding Concentricity |
μm |
≤ 0.5 |
|
Ububanzi Bokumboza (Okunganemibala) |
μm |
242±7 (okujwayelekile) |
|
μm |
200±10 (uma uthanda) |
||
Iphutha Le-Coating/Cladding Concentricity |
μm |
≤ 12 |
|
I-Curl |
m |
≥ 4 |
|
Ezemvelo (1310 nm , 1550 nm ) | |||
I-Temperature Cycling |
-60 ℃ ku +85 ℃ |
dB/km |
≤ 0.05 |
|
High Temperature & High Umswakama |
85℃, 85% RH, izinsuku ezingama-30 |
dB/km |
≤ 0.05 |
Ukucwiliswa emanzini |
23 ℃, izinsuku ezingu-30 |
dB/km |
≤ 0.05 |
Izinga Lokushisa Eliphezulu Ukuguga |
85℃, izinsuku ezingama-30 |
dB/km |
≤ 0.05 |
Omakhenikha | |||
Ubufakazi Ukucindezeleka |
- |
I-GPa |
0.69 |
I-Coating Strip Force * |
Isiqongo |
N |
1.3 - 8.9 |
Isilinganiso |
N |
1.0 - 5.0 |
|
Amandla Okuqina |
I-Fk=50% |
I-GPa |
≥ 4.00 |
Fk= 15% |
I-GPa |
≥ 3.20 |
|
Ukukhathala Okunamandla (Nd) |
- |
- |
≥ 20 |
Ukulahlekelwa Kwe-Macrobending | |||
Ø30 mm×10 t |
1550 nm |
dB |
≤ 0.25 |
1625 nm |
dB |
≤ 1.0 |
|
Ø20 mm×1 t |
1550 nm |
dB |
≤ 0.75 |
1625 nm |
dB |
≤ 1.5 |
|
* Amandla epeak amakhasi e-coating ngu-0.6-8.9N, futhi inani elijwayelekile lingu-0.6-5.0N lapho i-coatingdiameter ingu-200±10. | |||