| ʻĀpana | kūlana | Units | waiwai |
| Optical | |||
| Hoʻohaʻahaʻa | 1310 nm | dB/km | ≤ 0.350 |
| 1383 nm | dB/km | ≤ 0.350 | |
| 1550 nm | dB/km | ≤ 0.210 | |
| 1625 nm | dB/km | ≤ 0.230 | |
| Atenuation vs. Loʻihi hawewe | 1310 nm VS. 1285- 1330 nm | dB/km | ≤ 0.04 |
| 1550 nm VS. 1525- 1575 nm | dB/km | ≤ 0.03 | |
| Ka lōʻihi o ka hoʻopuehu Zero | - | nm | 1300-1324 |
| Kolo Puehu | ps/(nm2 ·km) | 0.073-0.092 | |
| Hoʻopuehu | 1550nm | ps/(nm ·km) | 13.3- 18.6 |
| 1625nm | ps/(nm ·km) | 17.2-23.7 | |
| Hoʻopuehu ʻia ke ʻano polarization (PMD) | - | ps/√km | ≤ 0.2 |
| Loʻihi hawewe ʻoki ʻoki λcc | - | nm | ≤ 1260 |
| Anawaena kahua (MFD) | 1310 nm | μm | 9.2±0.4 |
| 1550 nm | μm | 10.4±0.5 | |
| Hoʻokuʻu ʻia ʻana | 1310 nm | dB | ≤ 0.03 |
| 1550 nm | dB | ≤ 0.03 | |
| Geometrical | |||
| Anawaena hoopa'i | μm | 125±0.7 | |
| Hoʻopili ʻole i ka pōʻai | % | ≤ 1.0 | |
| Kupa/Cladding Concentricity Hapa | μm | ≤ 0.5 | |
| Ka anawaena o ka uhi (ʻaʻole kala) | μm | 242±7 (maʻamau) | |
| μm | 200±10 (koho) | ||
| Kupa/Cladding Concentricity Hapa | μm | ≤ 12 | |
| ʻOkuʻu | m | ≥ 4 | |
| Kaiapuni(1310nm, 1550nm) | |||
| Kaʻa Paʻa Paʻa | -60℃i ka +85℃ | dB/km | ≤ 0.05 |
| Kiekie Kiekie & Kiekie Haʻahaʻa | 85 ℃, 85% RH, 30 lā | dB/km | ≤ 0.05 |
| Ka Immersion Wai | 23 ℃, 30 lā | dB/km | ≤ 0.05 |
| ʻEleʻele i ka wela kiʻekiʻe | 85 ℃, 30 lā | dB/km | ≤ 0.05 |
| Mechanical | |||
| Hōʻike koʻikoʻi | - | GPa | 0.69 |
| ʻO ka ikaika o ka hoʻopaʻa ʻana * | Peak | N | 1.3 - 8.9 |
| Awelika | N | 1.0-5.0 | |
| Ikaika U'i | Fk=50% | GPa | ≥ 4.00 |
| Fk= 15% | GPa | ≥ 3.20 | |
| Ka luhi ʻana (Nd) | - | - | ≥ 20 |
| Nalo Macrobend | |||
| Ø30 mm×10 t | 1550 nm | dB | ≤ 0.25 |
| 1625 nm | dB | ≤ 1.0 | |
| Ø20 mm×1 hola | 1550 nm | dB | ≤ 0.75 |
| 1625 nm | dB | ≤ 1.5 | |
| * ʻO ka peak peel ikaika o ka uhi ʻana he 0.6-8.9N, a ʻo ka awelika waiwai he 0.6-5.0N i ka wā o ka coating diameter 200±10. | |||