G.657.A1. Ukugoba Ukungazweli kwimowudi enye yeFayibha yokubona
Iimeko zeSicelo
Iimpawu zokuSebenza
Ukucaciswa kweMveliso
| Ipharamitha | iimeko | Iiyunithi | ixabiso |
| I-Optical | |||
| Ukuthotywa | 1310 nm | dB/km | ≤ 0.350 |
| 1383 nm | dB/km | ≤ 0.350 | |
| 1550 nm | dB/km | ≤ 0.210 | |
| 1625 nm | dB/km | ≤ 0.230 | |
| Ukuthotywa vs. Wavelength | 1310 nm VS. 1285- 1330 nm | dB/km | ≤ 0.04 |
| 1550 nm VS. 1525- 1575 nm | dB/km | ≤ 0.03 | |
| I-Zero Dispersion Wavelength | - | nm | 1300-1324 |
| Zero Dispersion Slope | ps/(nm2 ·km) | 0.073-0.092 | |
| Ukusasazwa | 1550nm | ps/(nm ·km) | 13.3- 18.6 |
| 1625nm | ps/(nm ·km) | 17.2-23.7 | |
| Ukusasazwa kweNdlela yePolarization (PMD) | - | ps/√km | ≤ 0.2 |
| Ubude beWaveleng esisikiweyo λcc | - | nm | ≤ 1260 |
| I-Mode Field Diameter (MFD) | 1310 nm | μm | 9.2±0.4 |
| 1550 nm | μm | 10.4±0.5 | |
| Ukurhoxiswa Ukuyeka | 1310 nm | dB | ≤ 0.03 |
| 1550 nm | dB | ≤ 0.03 | |
| Yejometri | |||
| I-Cladding Diameter | μm | 125±0.7 | |
| I-Cladding Non-Setyhula | % | ≤ 1.0 | |
| Imposiso yoNxibelelwano engundoqo/yokugquma | μm | ≤ 0.5 | |
| Idayamitha yoKwaleka (Ayifakwanga mbala) | μm | 242±7 (umgangatho) | |
| μm | 200±10 (ukhetho) | ||
| Imposiso yokuNxibelelaniso/yokugquma | μm | ≤ 12 | |
| Curl | m | ≥ 4 | |
| Okusingqongileyo(1310nm, 1550nm) | |||
| Ubushushu bokukhwela ibhayisekile | -60℃ukuya +85℃ | dB/km | ≤ 0.05 |
| Ubushushu obuphezulu & Phezulu Ukufuma | 85℃, 85% RH, 30days | dB/km | ≤ 0.05 |
| Ukuntywiliselwa emanzini | 23℃, iintsuku ezingama-30 | dB/km | ≤ 0.05 |
| Ubushushu obuphezulu Ukuguga | 85℃, iintsuku ezingama-30 | dB/km | ≤ 0.05 |
| Oomatshini | |||
| Ubungqina boxinzelelo | - | GPA | 0.69 |
| I-Coating Strip Force * | Incopho | N | 1.3 - 8.9 |
| I-avareji | N | 1.0-5.0 | |
| Tensile strength | Fk=50% | GPA | ≥ 4.00 |
| Fk= 15% | GPA | ≥ 3.20 | |
| Ukudinwa ngamandla (Nd) | - | - | ≥ 20 |
| Ilahleko yeMacrobending | |||
| Ø30 mm×10 t | 1550 nm | dB | ≤ 0.25 |
| 1625 nm | dB | ≤ 1.0 | |
| Ø20 mm×1 h | 1550 nm | dB | ≤ 0.75 |
| 1625 nm | dB | ≤ 1.5 | |
| * I-peak peel force of the coating yi-0.6-8.9N, kwaye ixabiso eliqhelekileyo ngu-0.6-5.0N xa i-coatingdiameter i-200±10. | |||