G.657.A1. Bending Insensitive Single-mode Optical Fiber
Applikaasje senario's
Performance Features
Produkt Spesifikaasje
| Parameter | betingsten | Units | wearde |
| Optical | |||
| Attenuation | 1310 nm | dB/km | ≤ 0.350 |
| 1383 nm | dB/km | ≤ 0.350 | |
| 1550 nm | dB/km | ≤ 0,210 | |
| 1625 nm | dB/km | ≤ 0.230 | |
| Attenuation tsjin golflingte | 1310 nm VS. 1285-1330 nm | dB/km | ≤ 0,04 |
| 1550 nm VS. 1525-1575 nm | dB/km | ≤ 0,03 | |
| Zero dispersion golflingte | - | nm | 1300 - 1324 |
| Zero dispersion helling | ps/(nm2 ·km) | 0.073 - 0.092 | |
| Fersprieding | 1550 nm | ps/(nm ·km) | 13.3- 18.6 |
| 1625 nm | ps/(nm ·km) | 17.2-23.7 | |
| Polarisaasjemodusfersprieding (PMD) | - | ps/√km | ≤ 0.2 |
| Cut-off golflingte λcc | - | nm | ≤ 1260 |
| Mode Field Diameter (MFD) | 1310 nm | μm | 9,2±0,4 |
| 1550 nm | μm | 10,4±0,5 | |
| Attenuation Diskontinuïteit | 1310 nm | dB | ≤ 0,03 |
| 1550 nm | dB | ≤ 0,03 | |
| Geometrysk | |||
Bekleding Diameter |
μm |
125±0,7 |
|
Cladding Non-Circularity |
% |
≤ 1.0 |
|
Core / beklaaiïng Concentricity Flater |
μm |
≤ 0,5 |
|
Coating Diameter (ûnkleurd) |
μm |
242±7 (standert) |
|
μm |
200±10 (opsjoneel) |
||
Coating / Cladding Concentricity Flater |
μm |
≤ 12 |
|
Curl |
m |
≥ 4 |
|
Miljeu (1310 nm , 1550 nm ) | |||
Temperatuer Cycling |
-60 ℃ oant +85 ℃ |
dB/km |
≤ 0,05 |
|
Hege temperatuer & Heech Feuchte |
85 ℃, 85% RH, 30 dagen |
dB/km |
≤ 0,05 |
Wetter Immersion |
23 ℃, 30 dagen |
dB/km |
≤ 0,05 |
Hege temperatuer Aging |
85 ℃, 30 dagen |
dB/km |
≤ 0,05 |
Meganysk | |||
Bewiis Stress |
- |
GPa |
0.69 |
Coating Strip Force * |
Peak |
N |
1,3 - 8,9 |
Trochsneed |
N |
1,0 - 5,0 |
|
Treksterkte |
Fk=50% |
GPa |
≥ 4.00 |
Fk= 15% |
GPa |
≥ 3,20 |
|
Dynamic Fatigue (Nd) |
- |
- |
≥ 20 |
Macrobending ferlies | |||
Ø30 mm×10 t |
1550 nm |
dB |
≤ 0,25 |
1625 nm |
dB |
≤ 1.0 |
|
Ø20 mm×1 t |
1550 nm |
dB |
≤ 0,75 |
1625 nm |
dB |
≤ 1.5 |
|
* De peak peel krêft fan 'e coating is 0.6-8.9N, en de gemiddelde wearde is 0.6-5.0N as de coatingdiameter 200±10 is. | |||